Soft lithography

Figure 1 - "Inking" a stamp. PDMS stamp with pattern is placed in Ethanol and ODT (octadecanethiol) solution

Figure 2 - ODT from the solution settles down onto the PDMS stamp. Stamp now has ODT attached to it which acts as the ink.

Figure 3 - The PDMS stamp with the ODT is placed on the gold substrate. When the stamp is removed, the ODT in contact with the gold stays stuck to the gold. Thus the pattern from the stamp is transferred to the gold via the ODT "ink."

In technology, soft lithography refers to a family of techniques for fabricating or replicating structures using "elastomeric stamps, molds, and conformable photomasks".^[1] It is called "soft" because it uses elastomeric materials, most notably PDMS.

Soft lithography is generally used to construct features measured on the micrometer to nanometer scale. According to Rogers and Nuzzo (2005), development of soft lithography expanded rapidly from 1995 to 2005.

Advantages

Sarfus image of streptavidin deposited by soft lithography with PDMS stamp.

Soft lithography has some unique advantages over other forms of lithography (such as photolithography and electron beam lithography). They include the following:

• Lower cost than traditional photolithography in mass production
• Well-suited for applications in biotechnology
• Well-suited for applications in plastic electronics
• Well-suited for applications involving large or nonplanar (nonflat) surfaces
• More pattern-transferring methods than traditional lithography techniques (more "ink" options)
• Does not need a photo-reactive surface to create a nanostructure
• Smaller details than photolithography in laboratory settings (~30 nm vs ~100 nm). The resolution depends on the mask used and can reach 6 nm.^[2]

See also

• Nanolithography
• PDMS stamp
• Microcontact printing
• Multilayer soft lithography

References

1. ↑ In the words of Rogers and Nuzzo, p. 50, as cited in "References"
2. ↑ Waldner, Jean-Baptiste (2008). Nanocomputers and Swarm Intelligence. London: ISTE John Wiley & Sons. p. 93. ISBN 1-84704-002-0. 

Further reading

• Xia, Y.; Whitesides, G. M. (1998). "Soft Lithography". Angew. Chem. Int. Ed. Engl. 37 (5): 551–575. doi:10.1002/(SICI)1521-3773(19980316)37:5<550::AID-ANIE550>3.0.CO;2-G. 
• Xia, Y.; Whitesides, G. M. (1998). "Soft Lithography. In". Annu. Rev. Mater. Sci. 28: 153–184. Bibcode:1998AnRMS..28..153X. doi:10.1146/annurev.matsci.28.1.153. 
• Quake, S. R.; Scherer, A. (2000). "From micro- to nanofabrication with soft materials". Science. 290 (5496): 1536–1540. Bibcode:2000Sci...290.1536Q. doi:10.1126/science.290.5496.1536. PMID 11090344. 
• Rogers, J. A.; Nuzzo, R. G. (2005). "February). Recent progress in soft lithography. In". Materials today. 8 (2): 50–56. doi:10.1016/S1369-7021(05)00702-9. 

Nanolithography
Main	Optical Electron beam Nanoimprint Multi-Photon Scanning probe
Other	Molecular self-assembly Stencil X-ray Ion beam Magnetolithography Soft Laser printing Nanosphere Proton beam
See also	Nanotechnology Nanoelectronics