Spacer patterning

Spacer patterning flow: first pattern; deposition; spacer formation by etching; first pattern removal; etching with spacer mask; final pattern
Spacer trimming (top view). Left: Spacer (blue) is deposited on mandrel (gray) and etched, leaving only the portion covering the sidewall. Center: Mandrel is removed. Right: Spacer is trimmed by etching to smaller width.

Spacer patterning is a technique employed for patterning features with linewidths smaller than can be achieved by conventional lithography. In the most general sense, the spacer is a layer that is deposited over a pre-patterned feature, often called the mandrel. The spacer is subsequently etched back so that the spacer portion covering the mandrel is etched away while the spacer portion on the sidewall remains. The mandrel may then be removed, leaving two spacers (one for each edge) for each mandrel. The spacers may be further trimmed to narrower widths, especially to act as mandrels for a subsequent 2nd spacer formation. Hence this is a readily practiced form of multiple patterning. Alternatively, one of the two spacers may be removed and the remaining one trimmed to a much smaller final linewidth. Whereas immersion lithography has a resolution of ~40 nm lines and spaces, spacer patterning may be applied to attain 20 nm. This resolution improvement technique is also known as Self-Aligned Double Patterning (SADP). SADP may be re-applied for even higher resolution, and has already been demonstrated for 15 nm NAND flash memory.[1] Spacer patterning has also been adopted for sub-20 nm logic nodes, e.g., 14 nm and 10 nm.

Spacer Patterning Without Mandrel Removal

The mandrel is not removed after the spacer is etched to leave only the sidewall portion, in the case where the mandrel is the MOSFET gate stack. The silicon nitride sidewall spacer is retained to protect the gate stack and underlying gate oxide during subsequent processing.

Self-Aligned Anti-Spacer Double Patterning

An approach related derived from self-aligned spacer double patterning is so-called "anti-spacer" double patterning. In this approach a first layer coating the mandrel is eventually removed, while a second coated layer over the first layer is planarized and retained. A purely spin-on and wet-processed approached has been demonstrated.[2]

Spacer-Is-Dielectric (SID)

Spacers which define conducting features need to be cut to avoid forming loops. In the alternative spacer-is-dielectric (SID) approach, the spacers define dielectric spaces between conducting features, and so no longer need cuts. The mandrel definition becomes more strategic in the layout, and there is no longer a preference for 1D line-like features. The SID approach has gained popularity due to its flexibility with minimal additional mask exposures.[3] The anti-spacer double patterning approach described above naturally fits the SID approach since an additional layer is deposited after the spacer before its removal.

References

  1. J. Hwang et al., IEDM 2011, 9.1.1-9.1.4 (2011).
  2. M. Hyatt et al., Proc. SPIE 9051, 905118 (2014).
  3. Y. Du et al., "Spacer-Is-Dielectric-Compliant Detailed Routing for Self-Aligned Double Patterning Lithography", DAC 2013.
This article is issued from Wikipedia - version of the 4/13/2016. The text is available under the Creative Commons Attribution/Share Alike but additional terms may apply for the media files.